Product Description
Tianyi Polypropylene fiber (mesh) for cement concrete reinforced fiber products.
General idea:
TY-D modified polypropylene fiber for Changzhou Tianyi Engineering Fiber co.,LTD , which is a product of the company's independent research and development.
It is added in mortar or concrete in order to inhibit the plastic shrinkage crack of cement mortar and concrete before curing, and improving the quality of cement mortar and concrete, reducing maintenance costs, and extend the service life of the project.
Technical proposal:
The technology can be dispersed evenly in the concrete and play its effect for a long time by special anti-static and anti - ultraviolet treatment.The fiber "Y" section increases the surface area of the fiber.After chemical modification and physical modification, the surface of the fiber was rough and porous, which greatly improved the binding force of the fiber and cement.The monofilament polypropylene fiber is added into concrete base material, It can quickly and easily be mixed with mortar concrete materials.Because of the micro fiber, large the specific surface area ,It has nearly twenty fibers per cubic meter of concrete.Therefore, it can form a kind of chaos and support system.and effectively control concrete and cement mortar in the early plastic shrinkage of the production and development, dry shrinkage and other non structural cracks.Effectively preventing aggregate segregation and hinder the settlement crack formation. Greatly improving the concrete anti permeability, anti impact performance, increasing the toughness and wear resistance of the concrete, so that the life of the building is greatly prolonged.
The physical and chemical properties of the fiber used in the production of the technology:
The products can be produced according to your specifications.
| Fiber type |
Filament |
Density |
0.91g/cm 3 |
| Linear density |
14.5-18.9dtex |
Melting point |
165-175ºC |
| Breaking strength |
≥ 300MPa |
burning point |
590ºC |
| Elongation at break |
15%-20% |
Length |
6, 9,12 ,15 ,19mm~ |
| Modulus of elasticity |
≥ 3500MPa |
Acid and alkali |
Strong |
| Cross section shape |
Y type |
Phase volume diameter |
0.048mm |
Product Package:
Under normal circumstances
1,900g or 1000g / per film bag,12kg/Plastic woven bag, 1600kg/pallet.5.5 tons/1x20`gp,12tons/40"HQ,
2,Water soluble bag is also okay .
3,if you need special packages, We can help you to customize.
About Cooperation
L/C: 100% at sight L/C
T/T: 30% deposit by T/T,70% within 7 days after get the copy of B/L.
Paypal
Product Picture
Audited Supplier 
){kind=link}
){kind=link}