| Fiber Type: | Filament |
|---|---|
| Fiber Diameter: | 20-40um |
| Breaking Strength: | More Than 300MPa |
|
Still deciding? Get samples of US$ 0/kgs
Request Sample
|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
| Raw Material | 100% Polypropylene |
| Crack Elongation | 20+/-5% |
| Fiber Type | monofilament |
| Fiber Diameter | 20-30um |
| Melting Point(C Deg) | 160-170 |
| Density(g/cm3) | 0.91+/-0.01 |
| Acid&Alkali Resistance | Strong |
| Tensile Strength(Mpa) | >500 |
| Length | 3mm/6mm/9mm/12mm/19mm |
| Raw Material | 100% Polypropylene | Tensile Strength(MPa) | >500 |
| Crack Elongation | 20+/-5% | Length | 6mm/9mm/12mm/15m/19mm |
| Fiber Type | monofilament | Water absorbency | No |
| Fiber Diameter | 20-40um | Modulus of elasticity | ≥ 3500MPa |
| Melting Point(C Deg.) | 160 - 170 | Breaking strength | ≥ 300MPa |
| Density(g/cm3) | 0.91+/-0.01 | Melting point | 165-175ºC |
| Acid &Alkali Resistance | Strong | Burning point | 590ºC |
1. High grade concrete pavement and fencing, bridge, factory floor crack demanding project, it'll improve the service life of the pavement by 5 to 10 years.
1) Manufacturer/Factory
A,600g or 900g or 1000g / pe film bag, 18kg/ Plastic woven bag,8tons/1x20`gp,20tons/40"HQ
FAQ:
Q: Can I have a sample order?
){kind=link}